Successful high-efficiency energy conversion with organic monolayer on gold nanocluster surface

• Normally, when one photon is absorbed by a molecule, only one exciton (a bound state of an electron hole and an electron) is formed. However in recent years, singlet fission (which forms two excitons from the absorption process of a single photon) is gathering much attention worldwide, although significant work remains before it can be used in chemical reactions.
• In general, an organic molecule that has been chemically modified and integrated into the surface of metals loses significant excitation energy when compared to the isolated state of an organic molecule.
• In order to solve all of the above problems at once, a tetracene alkanethiol-modified gold nanocluster was newly designed and synthesized. An increase in lifetime of about 10,000 times was achieved by greatly suppressing the rapid loss of excitation energy on the metal surface. In addition, excitons were formed with high efficiency through singlet fission, and the efficiency of generating singlet oxygen was successfully improved to about 160% (fig. 1).

A research group comprising researchers from Keio University, Kobe University, and Tampere University focused on a photoreaction called singlet fission. This is a process in which two molecules positioned nearby interact with each other after one of the molecules absorbs a photon, forming two excitons. With the goal of solving the abovementioned problems all at once, they considered modifying tetracene (whose chemical structure is composed of four benzene rings connected in a straight line) into a metal nanocluster by the self-assembled monolayers (SAMs) method (fig.2). SAMs are monolayers made by chemically modifying organic ligands such as alkanethiol on the metal surface, and have been an important core technology for recent advancements in nanotechnology. In singlet fission, where reactions take place between two molecules located close to each other, the distance and orientation between the two molecules must be strictly controlled. When the surface of a gold nanocluster is chemically modified using tetracene homodisulfide (fig.2, right) that is composed of two tetracene alkanethiol with the same alkyl chains of length n, the probability of tetracene with the same alkyl chains of length n being placed in close proximity inevitably increases. Therefore, as shown on the left side of figure 2, tetracene heterodisulfide (Tc-C11-S-S-Cn-Tc) with different alkyl chain lengths (for which one had a length of n = 11 while the other had a length of n = 5, 7, or 9), were newly synthesized, and the gold nanocluster surface was chemically modified. Using tetracene heterodisulfide and tetracene homodisulfide, a series of tetracene alkanethiol-modified gold nanoclusters was synthesized (a block [cluster] of gold with 144 gold atoms whose surface was chemically modified by 60 tetracenes with alkanethiol as the medium). As a result, it was possible to create bimolecule arrangements with the optimal distance and orientation for singlet fission to occur efficiently on the gold nanocluster surface (while suppressing reverse reactions).